ANALISA KOEFISIEN DIFUSI ANODA LTO YANG DIDOPING Ca DARI LIMBAH KULIT TELUR UNTUK APLIKASI BATERAI LITHIUM-ION BERDAYA TINGGI
Abstrak
Telahdilakukansintesisanoda LTO doping Cadalambentuk Li4-xCaxTi5O12 (x =0%, 5%, 7.5%, dan 10%) menggunakanmetodesolid-state reaction. Limbahkulittelurdalambentuk CaCO3 dipilihsebagaisumberCadalam proses sintesis. Karakterisasistrukturdanimpedansielektrokimiasampeldilakukandengan XRD dan EIS. Karakterisasiserbuk Li4-xCaxTi5O12dengan XRD menunjukkanbahwatidakditemukannyakandungan CaCO3 dalamserbuk Li4-xCaxTi5O12 yangmenandakan atom Catelahberhasilmasukdalamstruktur LTO. Karakterisasi EIS menunjukkanbahwaperhitunganmenggunakanmetode Faraday, sampel Li4-xCaxTi5O12 dengannilai x = 10% mempunyaikoefisiendifusi paling tinggi di antarasemuasampelyaitu 1,469x10-12 cm2/s.
Teks Lengkap:
PDFReferensi
Oswal, Mehul. 2010. A comparative Study of Li-ion Batteries. University of Southern California.
Subhan, Achmad. 2011. FabrikasidanKarakterisasi Li4Ti5O12untukBahanAnodaBaterai Lithium Keramik. FTUI. Thesis.
Zhang, Qianyu, etal., Journal of Power Source 280 (2015) 355-362.
Laumann, Andreas. 2010. Nouvel Routes to Li4Ti5O12 : Characterization and Phase Relation. Ludwig-MaximiliansUniversitatMuenchen.
Li, Xing, et al.,ElectrochimicaActa 190 (2016) 69-75.
Liu, Hai-Ping, et al.,ElectrochimicaActa 192 (2016) 38-44.
Wang, Peng-fei, et al., Journal of Power Source 293 (2015) 33-41.
Li, Fuyun, et al., Int. J. Electrochem. Sci., 10 (2015) 10445-10453.
Wang, Wei, et al., ElectrochimicaActa 114 (2013) 198-204.
Zhang, Qianyu, et al., ElectrochimicaActa 98 (2013) 146-152.
Ding, Keqiang, et al., Int. J. Electrochem. Sci., 11 (2016) 446 – 458.
Zhang, Qianyu, et al.,Int. J. Electrochem. Sci., 8 (2013) 7816 – 7824.
He, Yan-Bing, et al., Journal of Power Source 239 (2013) 269-276.
Wang, Pengfei, et al.,Journla of Power Source 297 (2015) 383-294.
Li, Yueming, et al.,ElectrochimicaActa 182 (2015) 368-375.
Calcium Carbonate Content of Egg Shell. Oxford : New York
DOI: https://doi.org/10.24198/jmei.v7i02.11148
Refbacks
- Saat ini tidak ada refbacks.
##submission.copyrightStatement##