The effect of denture cleansing solution (H2O2) on the water solubility of self-cured acrylic resin

Irsan Ibrahim, Prima Luthfia, Widuri Julia Aryani

Abstract


Introduction: Denture cleanser must be able to remove bacterial plaque layers, eliminate food debris, with non-toxic properties. Denture cleansing was performed by immersing the denture into a solution of H2O2. Continuous denture wear can lead to plaque accumulation of Candida albicans colonies thus causes denture stomatitis. There was a slight dimensional stability difference of the self-cured acrylic base compared to the heat-cured after immersion in water. This study was aimed to analyse the effect of denture cleansing solution (H2O2) on the water solubility of self-cured acrylic resin. Methods: Twenty-four specimens of self-cured acrylic resin sized 15 x 20 x 2 mm, were divided into the control group (n = 12) and the treatment group (n = 12). All specimens were then immersed in the aquadest (control group) and H202(treatment group) for 6, 8, and 10 hours consecutively. Result: The average water solubility of self-cured acrylic resin soaked in H2O2 solution at 6 hours was 0.0007 µg/mm3; at 8 hours was 0.0011 µg/mm3; and at 10 hours was 0.0013 µg/mm3. The average water solubility of self-cured acrylic resin soaked in aquadest solution at 6 hours was 0.0013 µg/mm3; at 8 hours was 0.0080 µg/mm3; and at 10 hours was 0.0125 µg/mm3. Conclusion: The water solubility of the self-cured acrylic resin immersed in the H2O2 solution for 6, 8, and 10 hours was still below the ISO standard.

Keywords: Self-cured acrylic resin, H2O2, immersion time, water solubility.


Full Text:

PDF

References


Powers J, Sakaguchi R, editors. Craig's Restorative Dental Materials. 13th ed. MIssouri: Evolve; 2011. p. 257-70.

Noort RV. Introduction to Dental Materials. 4th ed: Mosby Elsevier; 2013. p. 219-22.

Anusavice K. Phillips’ science of dental materials. 11th ed. Missouri: Elsevier; 2012. p. 399-441.

Salim S. Perubahan Suhu Transisi Kaca dan Massa Resin Akrilik Heat Cured Akibat Kelembaban dan Lama Penyimpanan. Dent J (Maj Ked Gigi). 2014;47(3):173–7.

S.Togatorop R, F.Rumampuk J, Wowor VNS. Pengaruh Perendaman Plat Resin Akrilik Dalam Larutan Kopi Dengan Berbagai Kekentalan Terhadap Perubahan Volume Larutan Kopi. Jurnal e-GiGi (eG). 2017;5(1):19-23.

Sudhapalli S, Sudhapalli S. Time Dependent Effect of a Denture Cleanser on the Sorption and Solubility of Four Soft Liners-An Invitro Study. Journal of Clinical and Diagnostic Research : JCDR. 2016;10(4):ZC100-ZC3.p.1-6

Anonymous. Safety Data Sheet SR Triplex Hot Polimer: Ivoclar Vivadent; 2015 [updated 21 Oktober 2015; cited 2016 11 Oktober]. Safety Data Sheet SR Triplex Hot Polimer]. Available from: http://www.ivoclarvivadent.com/en/products/removable-denture-prosthetics/materials-for-dentures/sr-triplex-hot.

Kangsudarmanto Y, Rachmadi P, KF IWA. Perbandingan Perubahan Warna Heat Cured Acrylic Basis Gigi Tiruan. Dentino (Jur Ked Gigi). 2014;II(2):205-9.

Powers J, Sakaguchi R, editors. Craig's Restorative Dental Materials. 12 ed. MIssouri: Evolve; 2003. p. 190-201.

Anusavice K. Phillips’ science of dental materials. 11th ed. Missouri: Elsevier; 2006. p. 399-441.

Antolis M. Pengaruh Lama Perendaman Dalam Rebusan Daun Sirih (Piper Betle) Terhadap Kekuatan Transversal Resin Akrilik Self Cured [Skripsi]. Makasar: Universitas Hasanudin; 2014. p. 20-26

Sormin LTM, Rumampuk JF, Wowor VNS. Uji Kekuatan Transversal Resin Akrilik Polimerisasi Panas yang Direndam Dalam Larutan Cuka Aren. Jurnal e-GiGi (eG). 2017;5(1):30-4.

Sundari I, Sofya PA, Hanifa M. Studi Kekuatan Fleksural Antara Resin Akrilik Heat Cured dan Termoplastik Nilon Setelah Direndam Dalam Minuman Kopi Uleekareng (Coffea Robusta). J Syiah Kuala Dent Soc. 2016;1(1):51 - 8.

Setiawan D, Sibarani J, Suprihatin IE. Perbandingan Efektifitas Disinfektan Kaporit, Hidrogen Peroksida, dan Pereaksi Fenton (H2O2/Fe2+). Cakra Kimia (Indonesian E-Journal of Applied Chemistry). 2013. p. 20 - 30

O’Brien WJ, editor. Dental Materials and Their Selection. 4th ed. United States: Quintessence Publishing Co Inc.,U.S.; 2009. p. 147-9.




DOI: https://doi.org/10.24198/pjd.vol30no3.16114

Refbacks

  • There are currently no refbacks.


 

Creative Commons License All publications by the Universitas Padjadjaran [e-ISSN: 2549-6212, p-ISSN: 1979-0201] are licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.This license requires that reusers give credit to the creator. It allows reusers to distribute, remix, adapt, and build upon the material in any medium or format, for noncommercial purposes only.

Visitor Stat